top of page

Composition of materials

At Futurolab by Implant Design, our dental machining center works to ensure that our customers can receive reliable ans quality products.

All our products are C.E marked, they meet European legislation, particularly in terms of safety, hygiene and environmental protection.

Zircon Zirlux 16+
Coefficient of thermal expansion : 10.5 x 10-6 m/m·K (25–500°C)
Flexural strength  >1200 MPa (ISO6872)
Composition
ZrO2 + HfO2 + Y2O3 >98%
Fe2O3 <0.3%
Pr2O3 <0.3%
Er2O3 <0.3%
Autres oxydes <0.5%
Transparency 44%

Zircon multi-couches
Opéra Systèm Viva HT-ML
Thermal expansion (25-500°C)9,9
Flexural strength >1125 MPa
Composition
ZrO2 + HfO2,
Y2O3
Transparency 30.5%

Opéra Systèm Viva UT-ML
Thermal expansion (25-500°C)9,7
Flexural strength >557 Mpa
Composition
ZrO2 + HfO2
Y2O3 
Transparency 43.3 %

Cobalt-Chrome 
Density : 8.4 g/cm3
Melting temperature : 1307-1417°C
Fusion point : 1470°C
Unit load at break (Rp 0.2) : 395 MPa
Percentage of elongation at break : 11%
Elasticity module : 233 GPa
Hardness Vickers : 255 HV10
Colour: White
CET 25-500°C : 14.3 10-6K-1
Maximum cooking temperature : 980°C
Composition
Co 66% - Cr 27% - Mo 6% - Divers (Mn, Si) <1%
NF-EN-ISO 22674 de avril 2016
NF-EN-ISO 10993-5

Nanocéramique Enamic VITA

Composition

Polymères de résine 13-43%

Charge inorganique 55-85%

Additif <1%

Colorant <1%

Emax Vita

Composition

Céramique 100%

Titane Nicrallium TA6V-ELI
Density : 4.50g/cm3
Hardness : 330HV
Elastic limit in tension 0.2% : 795MPa
Tensile breaking stress : 860MPa
Elongation : 10%
CET : 20-500°C : 9.5 x10-6
Composition
Ti 90 % -AL 6 % - V 4 % - Fe < 0,25 % - Autres 0,25 %
NF-EN-ISO 22674 de avril 2016
NF-EN-ISO 5832.3